RTP 105 CC HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8U664A_RTP-105-CC-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Chemically Coupled - UL94 HB |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6550 | MPa | ASTM D638 |
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 to 6.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 157 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 30 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 101161 | RTP Company | PC | RTP |
| REVOLVE® N-261 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| Durethan® DP 1801/30 H3.0 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| LNP™ STAT-LOY™ PF306 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-LOY™ |
| CYCOLAC™ MG38U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |