Alathon® L5005V
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Tydk5_Alathon-L5005V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON L5005V is a high molecular weight high density copolymer that provides broad bimodal molecular weight distribution, high stiffness and good heat seal response and strength. Typical applications include merchandise bags, grocery sacks, trash can liners, produce bags and roll stock. Materials of animal origin are not used as plasticizers, additives, or raw materials in L5005V. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.060 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 13 µm | 945 | MPa | ASTM D882 |
| TD : 13 µm | 1050 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 34.5 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 29.0 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 84.1 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 57.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 320 | % | ASTM D882 |
| TD : Broken, 13 µm | 390 | % | ASTM D882 |
| Dart Drop Impact 1(13 µm) | 340 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 11 | g | ASTM D1922 |
| TD : 13 µm | 76 | g | ASTM D1922 |
| Extrusion instructions |
|---|
| Data Obtained Under the Following Extrusion Conditions:Alpine 200 mm 3 Layer Die (40/35/25); 3 Extruders: 65 mm / 75 mm / 50 mm; Die Gap = 1.5 mm; Film Thickness = 0.5 mil; 500 lbs/ hr; Internal Bubble Cooling; Neck Height = 8 x DD; Blow Up Ratio = 4:1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® P6 K25VA | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| Bayblend® M850 XF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Karina WHITE PVC COMPOUND 900D10/120-IS-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ OEL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ STAT-KON™ |
| OPNYL OP6GF33 | Ovation Polymers Inc. | Nylon 6 | OPNYL |