TAROLOX GFR 3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Tt0D0_TAROLOX-GFR-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT medium viscosity 15% glass fibres reinforced, heat stabilized, halogen free flame retardant UL94 V0, good flame proofing also at low thickness, good flow, good mechanical and thermal properties. High CTI value. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.70 - 1.0 | % | Internal method |
| Flow direction | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 | % | ISO 62 |
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Granule Humidity 1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 88.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 6000 | MPa | ISO 178 |
| Flexural Stress 3 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -25°C | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 35 | J/m | ASTM D256 |
| 23°C | 55 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 5.20 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Ball Pressure Test (205°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 120 to 130°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1502N (F30S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Nypol® PA A3 G20 HS PRTA011 NR446 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Huafon JF-P-9871 / JF-I-9818 (outsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Loyblend® TA-1300 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| Lustran® ABS PG298 | Styrolution | ABS | Lustran® ABS |