Beetle INJXT, IN JX/G
| Category: | Urea Formald , Urea Formaldehyde |
| Manufacturer: | BIP (Oldbury) Limited |
| Trademark: | Beetle |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Ts3cH_Beetle-INJXT-IN-JX-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Material suitable for a wide range of household articles such as Electrical accessories. Compared to standard Injection urea, INJC offers an improved stability for mouldings exposed to elevated temperatures. Its lower viscosity gives improved mould filling characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.74 | % | |
| -- 2 | 0.78 | % | |
| Water Absorption | ISO 62 | ||
| Cold 3 | 55.0 | mg | |
| Hot 4 | 260.0 | mg | |
| Post Shrinkage | ISO 2577 | ||
| -- 5 | 0.43 | % | |
| -- 6 | 0.41 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 115 | °C | DIN 43458 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.1 | kJ/m² | ISO 180/C |
| Unnotched Izod Impact Strength | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 133 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| -- 7 | 9.3 | kV/mm | |
| -- 8 | 8.0 | kV/mm | |
| Dissipation Factor | 0.025 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Preheated powder |
| 2 . | Cold powder |
| 3 . | 24 hr @ 23°C |
| 4 . | 30 min @ 100°C |
| 5 . | Cold powder |
| 6 . | (48 hr) Preheated powder |
| 7 . | (90°C) Preheated powder |
| 8 . | Cold powder |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1071 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| VECTRA® A530 | Celanese Corporation | LCP | VECTRA® |
| Zytel® 80G33HS1L BK104 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| CONTINUUM™ DGDD-2480 NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| Infino NH-1017D | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |