WanBlend® WHT-185ET8
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | WanBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Tks5k_WanBlend-WHT-185ET8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WHT-185ET8 is polyester-based TPU compound available in cylinder form that can solve a wide range of static decay, static shielding and electromagnetic shielding problems. Applications: Electronic component packaging, Pipes, Belts, Component trays, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.00 | MPa | |
| 300% Strain | 9.00 | MPa | |
| Tensile Strength | 22.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 620 | % | ASTM D412 |
| Tear Strength | 85.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -38.0 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 195 | °C | |
| Nozzle Temperature | 200 | °C | |
| Injection Pressure | 70.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 195 | °C | |
| Die Temperature | 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® E6426 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| Styrolution PS 1300/1301 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Abstron IM11GMS | Bhansali Engineering Polymers Limited | ABS | Abstron |
| LOXIM 830 02C HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| Opticarb 6085C | The Materials Group | PC+ABS | Opticarb |