GELOY™ XP4020R resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Te7Qt_GELOY-XP4020R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASA+PC may contain up to 20% post-industrial recycle. Excellent flow, weatherability, toughness and high heat for exterior uses. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 10 | g/10 min | |
| 230°C/3.8 kg | 22 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3030 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.7 | MPa | |
| Break | 44.1 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.7 | % | |
| Break | 36 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2550 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 69 | J/m | |
| 23°C | 300 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 22.6 | J | |
| 23°C, Total Energy | 33.9 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 107 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 90.0 | °C | |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 39 | mm/min | ISO 3795 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 98 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 98.9 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Nozzle Temperature | 238 to 254 | °C | |
| Processing (Melt) Temp | 254 to 271 | °C | |
| Mold Temperature | 54.4 to 71.1 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retelan® SF NERO | SO.F.TER. SPA | ABS | Retelan® |
| Tenac™-C 4563 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Smooth-On Psycho Paint® | Smooth-On, Inc | Silicone | Smooth-On |
| Vital-Line SHM5000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Hanwha Total PP BJ501X | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |