Ateva® 1070
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8TTSd4_Ateva-1070.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This is a multi-purpose resin commonly used for flexible packaging coextrusion to provide superior sealability, opticals, and strength, high quality microcellular crosslinked foam, extrusion, injection molding, and tubing applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 101 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882A | ||
| MD : Break | 17.0 | MPa | |
| TD : Break | 18.0 | MPa | |
| Tensile Elongation 2 | ASTM D882A | ||
| MD : Break | 400 | % | |
| TD : Break | 600 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 101 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® L 41003 | Reliance Industries Limited | HDPE | RELENE® |
| AMTOPP HCD18 | Inteplast Group | PP, Unspecified | AMTOPP |
| DENILUB Z 00U 4TF | Vamp Tech | PPA | DENILUB |
| HOPELEN SJ-160 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| LNP™ VERTON™ RV00CEXS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |