Sindustris PP HG3201SK2 is a Polypropylene material filled with 20% mineral. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PP HG3201SK2 are:
Typical application of Sindustris PP HG3201SK2: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.4 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1960 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 44.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| RTI Elec (1.50 mm) | 120 | °C | UL 746 |
| RTI Imp (1.50 mm) | 120 | °C | UL 746 |
| RTI Str (1.50 mm) | 120 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® LH 19001 | Plastic Solutions, Inc. | LLDPE | PrimaFlex® |
| Hylex® P1010 L2 HB | Entec Polymers | PC | Hylex® |
| Iupiace® GHF3010 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LG PVC LS170 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| LNP™ LUBRICOMP™ ZL003 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |