KumhoSunny PC/ABS HAC6010FG
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8T1mrO_KumhoSunny-PC-ABS-HAC6010FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAC6010FG is 10%GF reinforced flame retardan PC/ABS resin.HAC6010FG has high flame retardant properties and shrinking resistance properties.HAC6010FG is mainly used in printer, copy machine, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuye Z-500C | Shandong Xuye New Materials Co., Ltd. | CPVC | Xuye |
| AIE PA6 50G3F | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| KOCETAL® K300BLG | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina IVORY PVC COMPOUND 75920-35/1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostaform® UV90Z XAP2 ™ | Celanese Corporation | PPS | Hostaform® |