Hostaform® LM90
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8SUmH5_HostaformLM90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® LM90 is a nominal 9 melt flow rate acetal copolymer which is capable of being permanently marked by a laser. Parts molded from Hostaform® LM90 can be laser marked with barcodes, identification numbers, designs, 2-D symbology, etc. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 98.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 167 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 4.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J704LB | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Staramide PF003IX1 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| ASI POLYPROPYLENE 1329H-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| LUVOCOM® 1301-9017 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| Durethan® AM 40 X H2.0 DUS041 901510 | LANXESS GmbH | Nylon 66 | Durethan® |