Akulon® K225-KWS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8SU5Mn_Akulon-K225-KWS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K225-KWS is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific, Europe, or North America. Important attributes of Akulon® K225-KWS are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Across Flow | 1.0 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | 22 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 8.0 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | |
| 23°C | 60 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 9.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.30 | 8.00 | ||
| 1 MHz | 3.20 | 3.60 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 9.0E-3 | 0.13 | ||
| 1 MHz | 0.020 | 0.080 | ||
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.380 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 235 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2953-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TAIRIREX GP550N | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| ACCUTECH™ ABS831G30L | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| EMPILON庐 HN70 | EMPILON | SEBS | EMPILON® |
| LNP™ THERMOTUF™ RF002I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |