MEGOLON™ S500
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8RrI85_MEGOLON-S500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON™ S500 is a thermoplastic, halogen free, fire retardant cable sheathing compound for general purpose applications. It exhibits good processing characteristics - using a low compression, MEG type screw, processing speeds similar to those of PVC can be achieved. It can also be processed on a simple PVC screw at lower speeds. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| Mooney Viscosity (ML 1+4, 140°C) | 37 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 12.5 | MPa | IEC 60811-1-2 |
| -- | 11.0 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 2 | 150 | % | IEC 60811-1-2 |
| Break | 180 | % | IEC 60811-1-1 |
| Elongation at Break | |||
| after 4 hours, in IRM 902 Oil : 70°C | 200 | % | |
| after 4 hours, in SAE 20 Oil : 70°C | 210 | % | |
| after 7 days, in IRM 902 Oil : 23°C | 170 | % | |
| after 7 days, in IRM 903 Oil : 23°C | 160 | % | |
| Tensile Strength | |||
| after 4 hours, in IRM 902 Oil : 70°C | 10.0 | MPa | |
| after 4 hours, in SAE 20 Oil : 70°C | 8.50 | MPa | |
| after 7 days, in IRM 902 Oil : 23°C | 10.5 | MPa | |
| after 7 days, in IRM 903 Oil : 23°C | 9.50 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Elongation (-25°C) | 96 | % | IEC 60811-1-4 |
| Cold Impact (-25°C) | pass | IEC 60811-1-4 | |
| Hot Deformation (90°C) | 5.0 | % | BS 6469 99.1 |
| Hot Pressure Test (80°C) | 25 | % | IEC 60811-3-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | BS 6469 99.2 | ||
| 20°C | 5.0E+14 | ohms·cm | |
| after 12 hours immersion in water : 20°C | 2.0E+14 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 13.0 | µS/cm | IEC 60754-2 |
| Acid Gas Emission pH | 6.30 | IEC 60754-2 | |
| Flammability Temperature Index | 255 | °C | ISO 4589-3 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 3 | < 57 | Ds | |
| Non-flaming mode 4 | < 280 | Ds | |
| Toxicity | 1.50 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Ozone Resistance | pass | ASTM D470 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 6.50 | kN/m | BS 6469 99.1 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 12 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -18 | % | |
| Change in Tensile Stress | |||
| 23°C, 168 hr, in IRM 902 Oil | -5.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -14 | % | |
| 70°C, 4 hr, in IRM 902 Oil | -9.0 | % | |
| 70°C, 4 hr, in SAE 20 Oil | -26 | % | |
| Change in Tensile Strain at Break | |||
| 23°C, 168 hr, in IRM 902 Oil | -6.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -11 | % | |
| 70°C, 4 hr, in IRM 902 Oil | 11 | % | |
| 70°C, 4 hr, in SAE 20 Oil | 17 | % | |
| Change in Volume | |||
| 23°C, 168 hr, in IRM 902 Oil | 4.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | 20 | % | |
| 70°C, 4 hr, in IRM 902 Oil | 1.0 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (50 Hz) | 4.30 | ASTM D150 | |
| Dissipation Factor (50 Hz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 35 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 100°C |
| 2 . | after 7 days at 100°C |
| 3 . | Time to maximum: 7 minutes |
| 4 . | Time to maximum: 12 minutes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 30 TC BLACK | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| NYCOA Polyamide 2256 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Ad-Tech Polyester NO. 83 | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| DOMAMID® A1-002-V15-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| KYOCERA KE-850SP | KYOCERA Chemical Corporation | Epoxy | KYOCERA |