SABIC® PP 532B
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8RofUG_SABICPP532B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 532B has a high molecular weight and therefore mainly used for extrusion. It has been provided with a high heat stabilisation package and is typically used for thick sheet in demanding applications. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 | |
| Durometer Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% secant 1 | 1800 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 9.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | ISO 179/1eA |
| 0°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 25 | J/m | ASTM D256A |
| 0°C | 35 | J/m | ASTM D256A |
| 23°C | 60 | J/m | ASTM D256A |
| -20°C | 2.5 | kJ/m² | ISO 180/1A |
| 0°C | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed 4 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed 5 | 65.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 101 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Oxidation Induction Time | |||
| 200°C | > 60 | min | ISO 11357-6 |
| 200°C | > 60 | min | ASTM D3895 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | 标准 B (120°C/h), 压 力1 (10N) |
| 7 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE 2004 TN52 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| UPES® IP-73-UHP-LR | NOVA Chemicals | PS+PE | UPES® |
| Novodur® Ultra 4140PG | Styrolution | PC+ABS | Novodur® Ultra |
| King Pearl® G-3S | Loyal Chemical | PS (EPS) | King Pearl® |
| Karina NATURAL PVC COMPOUND 900-25/1-AYR-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |