Nypol® PA A3 V30 HL PRTA010 NR366
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8RYx44_Nypol-PA-A3-V30-HL-PRTA010-NR366.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 30% glass bead, good set of thermal and mechanical properties such as low warpage, resistance to compression, and excellent surface finish. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.90 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.75 | -- | % | ASTM D570 |
| Ash Content | 28 to 32 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 140 | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.0 | 12 | % | ASTM D638 |
| Flexural Modulus | 4500 | 2500 | MPa | ASTM D790 |
| Flexural Strength | 238 | 205 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 58 | 72 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 705 SI 2 | RTP Company | HDPE | RTP |
| Fortron® ICE 506L | Celanese Corporation | PPS | Fortron® |
| ELASTOSIL® LR 3092/65 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| EpoxAmite® 102 MEDIUM | Smooth-On, Inc | Epoxy | EpoxAmite® |
| SQUARE® LSG1001-08A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |