Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8RAM5k_Stat-Tech-Stat-Tech-X0300-8001-EDS-BK001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2070 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.0 to 10 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 91 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 139 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 133 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+8 to 5.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 0.794 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.15 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 290 to 310 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 10000 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Shandong PA1212 A1VS02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| AMTOPP BA30 | Inteplast Group | PP, Unspecified | AMTOPP |
| APEX® 90-A481R-90-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina RED COLOR CONCENTRATE 42/228-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |