Lastane 50 G/25
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8QP9QA_Lastane-50-G-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyurethane (PUR). Glass fibres. Very good noise reduction. Good impact resistance even at low temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.35 to 0.50 | % | |
| Flow : 2.00 mm | 0.25 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 25.0 | MPa | |
| Break, 23°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 35 | % | |
| Break, 23°C | 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 650 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 165 | °C | ISO 75-2/B |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 2(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALGLASS H 07 S 25 GT | RIALTI Srl | PP Homopolymer | RIALGLASS |
| Sup-tech A9705 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| NEXUS PC PC1510R | Nexus Resin Group, LLC. | PC | NEXUS PC |
| Clariant Nylon 6 6008-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| PLASTRON™ PAX-GF50-02 | Daicel Polymer Ltd. | Nylon, Unspecified | PLASTRON™ |