RheTech Polypropylene F40-01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8PS42X_RheTech-Polypropylene-F40-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass Fiber / Mineral Co-Reinforced, Chemically Coupled, Polypropylene, Black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 53.1 | MPa | ASTM D638 |
| Flexural Modulus | 5580 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Dart Drop Impact | 0.452 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 136 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 210 - 238 | °C | |
| Middle Temperature | 216 - 243 | °C | |
| Front Temperature | 221 - 249 | °C | |
| Nozzle Temperature | 227 - 238 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 137399 A NS | RTP Company | Polyester Alloy | RTP |
| RABALON® SJ8400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| ULTEM™ 2100R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| LNP™ LUBRICOMP™ OCP36F compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |
| PLUSTEK RA303G7 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |