Nypol® PA A3 G30 HS UV RH PRT0327 NR407
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8PLRuP_Nypol-PA-A3-G30-HS-UV-RH-PRT0327-NR407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color reinforced with 30% of fiberglass, heat stabilized, resistance to hydrolysis and UV. Good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 to 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.60 | -- | % | ASTM D570 |
| Relative Viscosity 1 | 46.0 to 52.0 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 200 | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 12200 | 6500 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 16 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength (-30°C) | -- | 70 | kJ/m² | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 11.0 | 14.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) (-30°C) | -- | 70.0 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | -- | °C | ASTM D648 |
| Peak Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 100 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Formic Acid |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® F FN51900 | LyondellBasell Industries | LDPE | Microthene® F |
| UBESTA XPA 9063 X1 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Next Nylon 66 Prime Series PXHS-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Lupoy® SR3108FM | LG Chem Ltd. | PC | Lupoy® |
| LNP™ THERMOCOMP™ LC003E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |