Ebalta GH 730 / BR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8OGnUn_Ebalta-GH-730-BR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GH 730/BR is a quite versatile two-components epoxy resin with good castability, curing at room temperature. Due to its easy workability as well as its high strength and low shrinkage there's a big variety of applications as mouldmaking, toolmaking and in foundries. Moreover the high impact resistance and cast thickness of more than 30 mm make even more applications possible. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.10 - 0.20 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 - 93 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 7400 - 8200 | MPa | ISO 178 |
| Flexural Stress | 75.0 - 85.0 | MPa | ISO 178 |
| Compressive Stress | 95.0 - 115 | MPa | ISO 604 |
| Taber Abrasion Resistance (500 Cycles, 500g, CS-17 wheel) | 19.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 4.0 - 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 - 66.0 | °C | ISO 75-2/B |
| CLTE - Flow (20 to 50°C) | 7.4E-5 | cm/cm/°C | DIN 53752 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 10 |
| Additional Information |
|---|
| Wear jet test : 151 W(V/t) [mm³/min] (internal tests) |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 2.15 - 2.25 | g/cm³ | |
| Viscosity (25°C) | 6.5 - 9.5 | Pa·s | |
| Curing Time (20°C) | 12 - 14 | hr | |
| Pot Life 1(20°C) | 35 - 45 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Advanced Composites ATX646M | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Edgetek™ QT-15GF/000 natur SO | PolyOne Corporation | SPS | Edgetek™ |
| Huafon JF-P-8465 / JF-I-4419 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Iupiace® AH70 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |