Jam PE 12XF6
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Jam Petrochemical Company |
| Trademark: | Jam PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ODXqz_Jam-PE-12XF6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jam PE 12XF6 is a Linear Low Density Polyethylene product. It is available in Africa & Middle East. Typical application: Film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.912 to 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 11.5 | MPa | |
| TD : Yield, 25 µm, Blown Film | 11.2 | MPa | |
| MD : Break, 25 µm, Blown Film | 43.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 35.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 600 | % | |
| TD : Break, 25 µm, Blown Film | 760 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 220 | g | |
| TD : 25 µm, Blown Film | 420 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 25 | ASTM D1790 | |
| Haze (25.0 µm, Blown Film) | 32 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom EP6333 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| ESTADIENE 0615 HHT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Escorene™ Ultra LD 730.09 Molding | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| HiFill® PA6 GF18 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LG PMMA HP05 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |