Badamid® LC70 M30 TM-Z3
| Category: | Nylon 6+Nylon 66/6 , Polyamide 6 + PA 66/6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8O3iGW_Badamid-LC70-M30-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LC70 M30 TM-Z3 is a Polyamide 6 + PA 66/6 (Nylon 6+Nylon 66/6) material filled with 30% mineral. It is available in Europe. Primary attribute of Badamid® LC70 M30 TM-Z3: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.6 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3900 | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 63.0 | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 20 | > 50 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 18 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 200 | -- | kJ/m² | |
| 23°C | 300 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 243 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 8.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.90 | 4.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.050 | IEC 60250 | |
| Comparative Tracking Index | 575 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| AMTOPP TL35 | Inteplast Group | PP, Unspecified | AMTOPP |
| DIC.PPS FZ-3600-L4 | DIC Corporation | PPS | DIC.PPS |
| GELAST GT30IT | Guang Sung Plastics (GSPL) | TP, Unspecified | GELAST |
| Hostacom BA742EC | LyondellBasell Industries | PP Copolymer | Hostacom |