Category: | PVDF , Polyvinylidene Fluoride |
Manufacturer: | SINOF HI-TECH MATERIAL CO. LTD |
Trademark: | SINOF |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 8N2x8a_SINOF-DH-F22E-2.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
DH-F22E-2 is one kind of pellet PVDF with higher MFR and suitable for making PVDF pipes, sheets and rods through extrusion. Products made from DH-F22E-2 have a wide range of service temperature (-50°C to 150°C). |
General Information | |
---|---|
Features |
|
Uses |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity 1 | 1.77 to 1.79 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 8.0 to 13 | g/10 min | ASTM D1238 |
Water Absorption (Equilibrium) | < 0.050 | % | ASTM D570 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 2 | ASTM D638 | ||
Yield, 23°C | > 35.0 | MPa | |
23°C | > 25.0 | MPa | |
Tensile Elongation 3 | ASTM D638 | ||
Yield, 23°C | > 10 | % | |
Break, 23°C | > 50 | % |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Peak Melting Temperature 4 | 164 to 172 | °C | ASTM D3418 |
Note Message | |
---|---|
1 . | 23°C |
2 . | 50 mm/min |
3 . | 50 mm/min |
4 . | 10°C/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
WELLAMID Nylon 6600 HWS | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
DILAMID® 66 GREY 2812 | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
Elastron® TPO T401.D51.B | Elastron USA, Inc. | TPO (POE) | Elastron® TPO |
EMOPLEN® A 1509 R G3 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
POLYfill PPHC K8030 | Polykemi AB | PP, Unspecified | POLYfill |