NYLOY® NG-0050N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8MwHLE_NYLOY-NG-0050N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® NG-0050N is a Polyamide 6 (Nylon 6) material filled with 50% glass fiber. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.34 | g/cm³ | ASTM D792 |
| -- | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.34 | % | |
| Across Flow | 0.91 | % | |
| Ash Content | 43 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 119 | ASTM D785 | |
| R-Scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 206 | MPa | ASTM D638 |
| -- | 198 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12400 | MPa | ASTM D790 |
| -- | 11000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 284 | MPa | ASTM D790 |
| -- | 300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 206 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR Polypropylene P4C5B-181B | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| ENFLEX VU-420-80A | ENPLAST, a Ravago Group Company | TPV | ENFLEX |
| KARIPRENE BLACK -E 4048/ 1-TRE | Karina Ind. e Com. de Plásticos Ltda | TPE | KARIPRENE |
| EPITEC® PC/ABS-308 | Osterman & Company | PC+ABS | EPITEC® |
| 3M™ Dyneon™ PTFE Compound FM 2370079 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |