| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Msdxq_CrastinSK605LMBK591.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Laser Markable, Polybutylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.1 | % | ISO 294-4 |
| Flow | 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | 54 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.75 mm | HB | IEC 60695-11-10, -20 | |
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| FMVSS Flammability | B | FMVSS 302 | |
| Atomization- F-value (refraction) | 99 | % | ISO 6452 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | 91.4 | µgC/g | VDA 277 |
| Odor | 3.00 | VDA 270 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 250 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Back Pressure | As low as possible | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ejection Temperature | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 30 - 130 | °C | |
| Holding Pressure | 60.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 6030NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| TOTAL Polypropylene PPH 10042 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| AKROMID® A3 GF 40 1 black (2386) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Axiall PVC HHP-190 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| JSR EPR EP02P | JSR Corporation | EPDM | JSR EPR |