KPOL-PP K-PPC 20.0

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8Mpd32_KPOL-PP-K-PPC-20-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is high impact block copolymer which has more ethylene contents than normal block copolymer, designed for injection molding applications, has excellent toughness and good dimensional stability. It is a controlled rheology grade.

Applications

KPOL® K-PPC 20.0 is a high melt flow rate heterophasic copolymer used for general purposes.

This product offers excellent processability, easy mould filling, productivity as well as good stiffness/impact strength balance (even at low temperature). Injection Molding of thick parts like housewares, paint pails, buckets, containers, battery cases, toys, etc.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Block Copolymer Controlled Rheology General Purpose Good Dimensional Stability Good Flow Good Impact Resistance Good Processability Good Stiffness Good Toughness Nucleated
Uses	Appliances Battery Cases Containers Household Goods Pails Thick-walled Parts Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	20	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	66		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	23.0	MPa	ASTM D638
Tensile Elongation ²(Break)	9.0	%	ASTM D638
Flexural Modulus - 1% Secant	960	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	50	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	86.0	°C	ASTM D648
Vicat Softening Temperature	147	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
ICORENE® N1005	ICO Polymers EMEA, A Division of A. Schulman	EVA	ICORENE®
Luranyl® HT 220 G6	ROMIRA GmbH	PPE+Nylon 66	Luranyl®
Pacrel® 6355N	Nanjing Jinling OPTA Polymer Co., Ltd.	TPV	Pacrel®
Sylvin 802-88 Green 3175	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
NORYL GTX™ GTX987 resin	SABIC Innovative Plastics	PPE+PS+Nylon	NORYL GTX™