Zytel® 73G30L NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8MF7rO_Zytel-73G30L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.3 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.9 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9800 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 6.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 5500 | MPa | |
| 1000 hr | -- | 4400 | MPa | |
| Flexural Modulus | 8200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | -- | kJ/m² | |
| -30°C | 11 | 21 | kJ/m² | |
| 23°C | 16 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 84 | kJ/m² | |
| 23°C | 100 | 97 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 11 | -- | kJ/m² | |
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 15 | 20 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | 100 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.4E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 25 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daicel PP PG2N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Etinox® EI-9320 | Ercros, S.A. | PVC, Flexible | Etinox® |
| HIPOL™ J850Y | Mitsui Chemicals, Inc. | PP Random Copolymer | HIPOL™ |
| Hylac® EX18 | Entec Polymers | ABS | Hylac® |
| LNP™ LUBRICOMP™ OCL36 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |