DINALON® PA 6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8LeXIM_DINALON-PA-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON®PA 6 is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 180 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Glow Wire, UNE 20-672-83: 650°CVicat Softening Temperature, ASTM D1525: >180°CDTUL, ASTM D648: 50°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4PROP® 9C23200 | 4Plas | PP Copolymer | 4PROP® |
| BESTNYL SE30VI02AH | Triesa Plastics | Nylon 66 | BESTNYL |
| KPOL-HDPE HD K-I 9/956 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| INEOS PP R55C-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LUVOCOM® 1-7321-5 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |