Lusep® SP2306F
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lusep® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Ivrnf_Lusep-SP2306F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Flame Retardant Application Pump Units, Pick-up Lends Holder, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 113 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 9320 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm 5 | 260 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm 6 | 230 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 31 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 400 to 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 150 | °C | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 4.6kg |
| 6 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNEL® U3500 | Tyne Plastics LLC. | PEI | TYNEL® |
| LNP™ LUBRICOMP™ D20001 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| OmniLon™ PA6/6 U GR23 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| SQUARE® LIM1939-56AE/BE | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Elastoflex® W 5666/103 | BASF Polyurethanes GmbH | PUR-MDI | Elastoflex® |