Starex NH-1926
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Itid5_Starex-NH-1926.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-halogen flame-retardant HIPS with the characteristic of high-impact that can be applied to the exterior material of TV and VCR and interior/exterior material of OA devices |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 11 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 10 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 26.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2000 | MPa | ASTM D790 |
| -- 3 | 2120 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 36.0 | MPa | ASTM D790 |
| -- 5 | 44.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 120 | J/m | ASTM D256 |
| 23°C 6 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 73.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 84.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIMID® N66-G13LU | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Unipren® Elastomers B3 PRTA010 55A UP314 | Petropol Industry and Trade of Polymers LTDA | TPV | Unipren® Elastomers |
| Natur-Tec® BF3001J | Natur-Tec - Northern Technologies International Corp | Biodeg Polymers | Natur-Tec® |
| Evoprene™ HP 3704 | AlphaGary | SBC | Evoprene™ HP |
| Geon™ Vinyl Rigid Extrusion 78761 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |