Order Products : sales@su-jiao.com
UmaPET SI
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8IiXdt_UmaPET-SI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0100 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0120 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0150 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0230 mm | 2.5 | % | |
| Across Flow : 150°C, 30 min, 0.0100 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0150 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0230 mm | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.35 | ||
| vs. Itself - Dynamic 2 | 0.35 | ||
| vs. Itself - Dynamic 3 | 0.35 | ||
| vs. Itself - Dynamic 4 | 0.35 | ||
| vs. Itself - Static 5 | 0.40 | ||
| vs. Itself - Static 6 | 0.40 | ||
| vs. Itself - Static 7 | 0.40 | ||
| vs. Itself - Static 8 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 10 12 15 23 | µm | |
| Film Thickness - Recommended / Available | 10, 12, 15, 23 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 10 µm | 206 | MPa | |
| MD : Break, 12 µm | 206 | MPa | |
| MD : Break, 15 µm | 186 | MPa | |
| MD : Break, 23 µm | 186 | MPa | |
| TD : Break, 10 µm | 216 | MPa | |
| TD : Break, 12 µm | 216 | MPa | |
| TD : Break, 15 µm | 206 | MPa | |
| TD : Break, 23 µm | 206 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 10 µm | 100 | % | |
| MD : Break, 12 µm | 100 | % | |
| MD : Break, 15 µm | 100 | % | |
| MD : Break, 23 µm | 100 | % | |
| TD : Break, 10 µm | 90 | % | |
| TD : Break, 12 µm | 90 | % | |
| TD : Break, 15 µm | 90 | % | |
| TD : Break, 23 µm | 90 | % | |
| Yield | Internal Method | ||
| 10.0 µm | 71.4 | m²/kg | |
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ash Pick Up Test | Internal Method | ||
| 10.0 µm | Pass | ||
| 12.0 µm | Pass | ||
| 15.0 µm | Pass | ||
| 23.0 µm | Pass | ||
| Surface Static Charge 9 | Internal Method | ||
| 10.0 µm | Nil | ||
| 12.0 µm | Nil | ||
| 15.0 µm | Nil | ||
| 23.0 µm | Nil | ||
| Wetting Tension - Plain side | ASTM D2578 | ||
| 10.0 µm | 44 | dyne/cm | |
| 12.0 µm | 44 | dyne/cm | |
| 15.0 µm | 44 | dyne/cm | |
| 23.0 µm | 44 | dyne/cm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 10.0 µm | 3.5 | % | |
| 12.0 µm | 3.5 | % | |
| 15.0 µm | 3.5 | % | |
| 23.0 µm | 4.5 | % |
| Note Message | |
|---|---|
| 1 . | 12 µm |
| 2 . | 10 µm |
| 3 . | 15 µm |
| 4 . | 23 µm |
| 5 . | 10 µm |
| 6 . | 12 µm |
| 7 . | 15 µm |
| 8 . | 23 µm |
| 9 . | Hand held static locator |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PS High Impact IS300 | M. Holland Company | PS (HIPS) | MTEGRITY™ PS High Impact |
| TOTAL Polypropylene PPH 3429 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Vyncolit® 2950W | Vyncolit N.V. | Phenolic | Vyncolit® |
| Hostaform® AM90S | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| HIPEX® HX8IDN (Series: HTR/OR) | KRAIBURG TPE | TPE | HIPEX® |