POLYFORT® FPP 1310
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8IZvvN_POLYFORT-FPP-1310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20% Mica |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 4 | 2700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 115 | °C | |
| 1.8 MPa, Unannealed | 58.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 21 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® ESD 7100 | Premix Oy | ABS | PRE-ELEC® |
| Star L PA6 D51 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Hostacom TKC 156N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Karina ICE COLOR PVC COMPOUND -E 798-P-28/ 37-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LSG2522-18 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |