Zytel® PLUS PLS95G40DH1T BK261
| Category: | Nylon, Unspecified , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8IOB7m_Zytel-PLUS-PLS95G40DH1T-BK261.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass Reinforced, Heat Stabilized, Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 277 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 16 | kJ/m² | |
| 23°C | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 110 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 263 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 500P | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| DJSilicone NE-9440 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Dynacom 401-G35 | Dynachem Co. Ltd. | Nylon 6 | Dynacom |
| Plaskon MUF-2A LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| XANTAR® LDS 3735 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® LDS |