Order Products : sales@su-jiao.com
Catalyst F/AC
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Catalyst |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8I6dRe_Catalyst-F-AC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Catalyst CT/7-LR UV is a polyolefin masterbatch, which is used as cable silane crosslinkable mixture according to the recommended dosage. specially designed for Polidan®Polidiemme®And Cogegum®Developed for GFR series compounds, it is suitable for most harsh long-term aging environments, has low catalytic activity, and has better UV/VIS resistance and aging resistance. The catalyst CT/7-LR UV has a wide range of applications due to its catalytic activity and anti-aging effect on the final product. Contains metal passivator and can directly contact untinned copper. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792 |
| Apparent Density 2 | 0.66 | g/cm³ | ISO 60 |
| Carbon Black Content | > 35 | % | ASTM D1603 |
| Additional Information |
|---|
| 存储产品必须按下列条件存储：-密封，包装袋完好 环境温度不超过35°C -避免在阳光下曝晒和露天放置 存放时间过长会造成产品性状改变。 保质期：12个月 如果没有满足上述条件，苏威特种聚合物不承担任何责任。 存放时间过长会造成产品性状改变。苏威特种聚合物建议按照包装印制生产日期，在12个月内使用完毕。如果没有满足上述条件，苏威特种聚合物不承担任何责任。包装-采用防潮袋包装，每袋25kg，或1375kg堆放于货板供应。-1000kg纸箱包装 |
| Note Message | |
|---|---|
| 1 . | Test on the press plate |
| 2 . | Particle test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1130B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Selon 710 | Soredi S.p.a. | PC | Selon |
| Fainplast PVC PH 75/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Epoxies, Ect. 10-3008 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| ESTADIENE 1030 T V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |