Lumiloy® GP2300
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8GbRa4_Lumiloy-GP2300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, General Purpose Description GF 30% Reinforced, NSF Certified for Black and Grey, High Impact Strength, Hydrolytic Stability Application Electric and Electronic Parts, Part for Water contact, Water Pump Housing or Impellers |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 127 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 6960 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 3.20 mm) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 135 | °C | ASTM D648 |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 5 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 130°C | 1.7E-5 | cm/cm/°C | |
| Transverse : -30 to 130°C | 7.0E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 36 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 4.00 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | > 0.030 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Nozzle Temperature | 270 to 310 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ RN0611 resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| NYCOA Polyamide 2063 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| Canuck Compounds 800 Series - BK 8-5-8 | Canuck Compounders Inc. | Polyolefin, Unspecified | Canuck Compounds |
| Daelim Po1y® TR-420 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Karina IVORY PVC COMPOUND 105852-35/1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |