Celanex® XFR 6842 GF10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8GBBcT_CelanexXFR6842GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex XFR 6842 GF10 is a halogen and antimony free flame retardant (V-0 @ 0.4 mm) 10% glass reinforced PBT grade with good processability and no corrosive emissions during processing. It is suitable for parts requiring enhanced tracking resistance, toughness, and flame retardancy at <0.75 mm wall thickness. The product is WEEE and RoHS compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.0 - 1.2 | % | ISO 294-4 |
| Flow | 1.1 - 1.3 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 81 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 173 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | IEC 60250 | |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.40 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S HS 105 M NAT | Radici Plastics | Nylon 6 | Radilon® |
| Nilac TR F17 V0 | Soredi S.p.a. | ABS | Nilac |
| ACCUTECH™ HP0334C40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| GAPEX® RPP25EA32BL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Enviramid® N2330STHL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |