LNP™ LUBRICOMP™ LCL33EXQ compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8FzGpg_LNP-LUBRICOMP-LCL33EXQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding. Also known as: LNP* LUBRICOMP* Compound LCL33EXQ Product reorder name: LCL33EXQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 30.0 | cm³/10min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16000 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 185 | MPa | ASTM D638 |
| Break | 181 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.8 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 13400 | MPa | ASTM D790 |
| -- 5 | 13500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 276 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 277 | MPa | ASTM D790 |
| Poisson's Ratio | 0.43 | ISO 527-2 | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.37 | ||
| vs. Itself - Static | 0.35 | ||
| Wear Factor - Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 7 | 5.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 320 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -30 to 150°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -30 to 150°C | 5.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 430BE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| HiFill® PA12 CL | Techmer Engineered Solutions | Nylon 12 | HiFill® |
| Kumho KTR KTR 655 | Korea Kumho Petrochemical Co., Ltd. | SBS | Kumho KTR |
| Karina RED COLOR CONCENTRATE -E 42/268-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ QD000I compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |