ELEVATE™ EB502
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8FqgwV_ELEVATE-EB502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Westlake Elevate™ EB502 resin is a fractional melt index 12.5% VA ethylene vinyl acetate copolymer designed for flexible packaging and other films that require excellent toughness and good heat sealing characteristics. This resin has excellent low temperature brittleness properties, melt strength, and flexibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 12.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 51 µm, Blown Film | 75.8 | MPa | |
| 1% Secant, TD : 51 µm, Blown Film | 89.6 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 51 µm, Blown Film | 27.6 | MPa | |
| TD : Break, 51 µm, Blown Film | 29.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 51 µm, Blown Film | 450 | % | |
| TD : Break, 51 µm, Blown Film | 950 | % | |
| Dart Drop Impact (51 µm, Blown Film) | 580 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 76.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 94.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (50.8 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 to 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B4406 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Braskem PE ML3600S | Braskem | LLDPE | Braskem PE |
| Fainplast PVC PG 55/A | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Edgetek™ AT-30GF/000 BLACK | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| KYOCERA TCG1604 | KYOCERA Chemical Corporation | TS, Unspecified | KYOCERA |