EBAC® SP1802

Category:	EnBA , Ethylene n-Butyl Acrylate Copolymer
Manufacturer:	Westlake Chemical Corporation
Trademark:	EBAC®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8FX2k9_EBAC-SP1802.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
EBAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. These resins are less crystalline and softer than polyethylenes. They are non-corrosive at extrusion temperatures and have excellent thermal stability over the full processing temperature range.

General Information
Features	Copolymer Good Adhesion Good Flexibility Good Heat Seal Good Thermal Stability Good Toughness Heat Sealable Low Temperature Toughness Soft
Uses	Containers Film Medical/Healthcare Applications Packaging
Forms	Pellets
Processing Method	Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.927	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.50	g/10 min	ASTM D1238
n-Butyl Acrylate Content	22.5	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	40		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Break)	13.0	MPa	ASTM D638
Tensile Elongation ²(Break)	850	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -73.0	°C	ASTM D746
Vicat Softening Temperature	59.0	°C	ASTM D1525
Peak Melting Temperature	86.0	°C	ASTM D3418

Note Message
1 .	Type IV, 500 mm/min
2 .	Type IV, 500 mm/min

Resin Grade	Manufacturer	Category	Trademark
UNITHENE® LH506	USI Corporation	HDPE	UNITHENE®
NEOFLON™ AC-5820	DAIKIN AMERICA, INC.	PFA	NEOFLON™
Eastar™ DN004HF	Eastman Chemical Company	Copolyester	Eastar™
LONOY lonoy 6100	Kingfa	PC+PBT	LONOY
Plasmer 1380N/1002	HYUNDAI EP Co., Ltd.	TPE	Plasmer