LNP™ LUBRICOMP™ RL004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8EN4gm_LNPLUBRICOMPRL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RL004 is a compound based on Nylon 66 resin containing PTFE. Also known as: LNP* LUBRICOMP* Compound RL-4040 Product reorder name: RL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 24.0 - 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 1.8 - 2.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 58.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus 2 | ISO 178 | ||
| -- | 2700 | MPa | ISO 178 |
| 60°C | 1400 | MPa | ISO 178 |
| 100°C | 700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 82.0 | MPa | ISO 178 |
| 60°C | 35.0 | MPa | ISO 178 |
| 100°C | 18.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.32 | ASTM D3702 Modified | |
| With Self-Static | 0.21 | ASTM D3702 Modified | |
| Flexural Strain at Break 3 | ISO 178 | ||
| -- | 7.0 | % | ISO 178 |
| 60°C | 7.0 | % | ISO 178 |
| 100°C | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 16.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, unannealed, 64.0mm span | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 74.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1182A | Teknor Apex Company | TPE | Telcar® |
| TITANPRO® SM461 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| EXCELLOY EKF55 | Techno Polymer Co, Ltd. | ABS | EXCELLOY |
| HiFill® PA6 GF33 IM L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Lionpol HF-204567 | Lion Polymers Incorporated | TPE | Lionpol |