ACRYLITE® Sheet Optical MR
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8EGALR_ACRYLITE-Sheet-Optical-MR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® Optical (MR) sheet is a continuously manufactured acrylic sheet that has excellent abrasion and chemical resistant properties with outstanding optical quality. It is available with coating on one side or two sides. While two-side coated sheet provides maximum protection, one-side coated sheet offers economical advantages for applications where only one side of the sheet is exposed. In addition, the uncoated side is ideal for silk screening. Applications ACRYLITE® Optical (MR) sheet is ideal for a wide variety of applications including: One-Sided Coating
Two-Sided Coating
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 91.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 25 | mm/min | ASTM D635 |
| Self Ignition Temperature | 443 | °C | ASTM D1929 |
| Smoke Density | 1.0 | % | ASTM D2843 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 92.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Abrasion Resistance of the Coating Rotary Brass Wool (25 cycles) : < 1% Change in Haze (Proprietary method) Taber Abrasion (100 cycles) : < 2% Change in Haze (ASTM D1044) Falling Sand (3,000 grams) : < 10% Change in Haze (DIN 52348) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Ultradur® B 4300 K6 | BASF Corporation | PBT | Ultradur® |
| Chemraz 520 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Grilamid® LV-30H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Sylvin 916VO-95 Yellow 449 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |