LNP™ THERMOCOMP™ RB006 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8EAY1y_LNP-THERMOCOMP-RB006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead. Also known as: LNP* THERMOCOMP* Compound RB-1006 Product reorder name: RB006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| -- | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.72 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.72 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6810 | MPa | ASTM D638 |
| -- | 7290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 66.9 | MPa | ASTM D638 |
| Break 2 | 58.0 | MPa | ASTM D638 |
| Break | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break 3 | 6.5 | % | ASTM D638 |
| Break | 7.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4060 | MPa | ASTM D790 |
| -- | 4700 | MPa | ASTM D790 |
| -- 5 | 3850 | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | ||
| -- | 124 | MPa | |
| Break, 50.0 mm Span 6 | 87.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 7 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 390 | J/m | ASTM D4812 |
| 23°C 8 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 101 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 92.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 95.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 126217 Z | RTP Company | PLA | RTP |
| Mirakutoran® TPU E660MNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Ultramid® A3EG7 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Clariant Acetal HP-MF5 | Clariant Corporation | Acetal (POM) Homopolymer | Clariant Acetal |
| Durethan® AKV 35 HR H2.0 901510 | LANXESS Corporation | Nylon 66 | Durethan® |