Amodel® A-4160 HSL

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8DSPX9_Amodel-A-4160-HSL.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Amodel A- 4160 HSL resin is a 60% glass fiber reinforced thermally stable polyphthalamide (PPA) with high elastic modulus, high thermal deformation temperature and excellent creep resistance at high temperature. It is specially developed for metal substitute materials. Rapid crystallization and good fluidity can shorten the molding cycle and improve the molding efficiency.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 60% filler by weight
Additive	heat stabilizer Lubricant demoulding
Features	Super rigidity Good dimensional stability Low CLTE High strength Fast molding cycle Good creep resistance Good chemical resistance Heat resistance, high Hot water formability Thermal Stability Good toughness Lubrication
Uses	Transfer application Electrical/Electronic Applications Industrial application Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field Mobile phone Shell Camera application
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Water temperature mold injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)

Physical	Nominal Value	Unit	Test Method
Density	1.75	g/cm³	ISO 1183/A
Molding Shrinkage			ISO 294-4
Vertical flow direction	0.80	%	ISO 294-4
Flow direction	0.50	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.19	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-2
23°C	23300	MPa	ISO 527-2
200°C	8770	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	244	MPa	ISO 527-2
Fracture, 200°C	79.6	MPa	ISO 527-2
Tensile Strain			ISO 527-2
Fracture, 23°C	1.4	%	ISO 527-2
Fracture, 200°C	3.3	%	ISO 527-2
Flexural Modulus			ISO 178
23°C	19300	MPa	ISO 178
200°C	8500	MPa	ISO 178
Flexural Stress			ISO 178
23°C	385	MPa	ISO 178
200°C	137	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	13	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	130	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	304	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Rear Temperature	318 - 324	°C
Front Temperature	327 - 332	°C
Processing (Melt) Temp	329 - 343	°C
Mold Temperature	65.6 - 93.3	°C

Injection instructions
射出压力：3~4英寸/秒

Resin Grade	Manufacturer	Category	Trademark
RAMCLEAN™ 204	Polyram Ram-On Industries	TP, Unspecified	RAMCLEAN™
3M™ Dyneon™ PTFE Compound TFX 4262	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound
AMTOPP CH20	Inteplast Group	PP, Unspecified	AMTOPP
KOPA® KN133G10	Kolon Plastics, Inc.	Nylon 6	KOPA®
Jam HDPE HM9455F	Jam Petrochemical Company	HDPE	Jam HDPE