Petrothene® NA205000X01
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8D7fvM_Petrothene-NA205000X01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA205000X01 is an extrusion coating resin especially recommended for high-speed, light weight coating applications. The resin can be drawn to a 3 lb/ream coating weight at line speeds in excess of 1,500 fpm with minimum neck-in and no edge weave. It is recommended for locker wraps, sugar pouches, industrial and multi-wall bags and laminations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 10.3 | MPa | ASTM D638 |
| Tensile Elongation 1(Break) | 640 | % | ASTM D638 |
| Flexural Modulus | 212 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 310 - 327 | °C |
| Extrusion instructions |
|---|
| It is recommended that a melt temperature of 590°F - 620°F be used for light-weight coating applications in conjunction with electrostatic, flame or chemical priming to insure good adhesion. The maximum recommended melt temperature for NA205000X01 is 625°F. |
| Note Message | |
|---|---|
| 1 . | Type 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4807 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® LDPE 1922N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| ExxonMobil™ PP9513 | ExxonMobil Chemical | PP Random Copolymer | ExxonMobil™ |
| ESPOLEX WT485 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| KumhoSunny PA/PPE HAP8940 | Shanghai KumhoSunny Plastics Co., Ltd. | Nylon+PPE | KumhoSunny PA/PPE |