DOW™ LLDPE DFDC-7080 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Cw3wK_DOW-LLDPE-DFDC-7080-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow Linear Low Density Polyethylene DFDC-7080 NT 7 is a Linear Low Density Polyethylene Resin material,. This product is available in North America and is processed by blowing film. The main characteristics of Dow linear low density polyethylene DFDC-7080 NT 7 are:
|
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | Internal method |
| Film Puncture Energy | 1.58 | J | |
| Film Puncture Force | 31.1 | N | |
| Film Puncture Resistance | 7.78 | J/cm³ | |
| Film strength | ASTM D882 | ||
| MD | 99.3 | J/cm³ | ASTM D882 |
| TD | 105 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 223 | MPa | ASTM D882 |
| 2% secant, MD | 185 | MPa | ASTM D882 |
| 1% secant, TD | 216 | MPa | ASTM D882 |
| 2% secant, TD | 177 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.4 | MPa | ASTM D882 |
| TD : Yield | 11.4 | MPa | ASTM D882 |
| MD : Fracture | 29.0 | MPa | ASTM D882 |
| TD : Fracture | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 650 | % | ASTM D882 |
| TD : Fracture | 660 | % | ASTM D882 |
| Dart Drop Impact | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 190 | g | ASTM D1922 |
| TD | 370 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ISO 306 |
| Melting Temperature (DSC) | 122 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 19 | ASTM D2457 | |
| Haze | 37 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5in.; 30:1ratio L/D Screw Type: DSB II Die Gap: 70 mil (1.8 mm) Melt Temperature: 415°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 39 rpm Frost Line Height: 54 in. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 11PG1 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| AKROMID® B3 GF 30 S3 natural (2984) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| EcoBlend® HCL7120 | Shanghai KumhoSunny Plastics Co., Ltd. | PLA+PMMA | EcoBlend® |
| Plexiglas® V044 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 8240-90 White 1543 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |