ASTALAC™ ABS LXB
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8BgogA_ASTALAC-ABS-LXB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS LXB is an ultra high impact strength grade of ABS and is designed for injection moulding applications requiring the highest toughness and abuse resistance whilst maintaining a balance of product rigidity and mouldability. Typical automotive applications include painted bumper bars assemblies, lower bodyside cladding panels and decorative side skirts. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS LXBUV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1850 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 59.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 430 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 35.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 74.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 79.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 85.0 | °C | |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0207LA | Borealis AG | Plastomer | Queo™ |
| SUMIKASUPER® LCP E6406 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| DAI-EL™ G-797 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina WHITE PVC COMP E 880-10/136-A-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pacrel® 6365N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPV | Pacrel® |