Category: | LDPE+LLDPE , Low Density Polyethylene + LLDPE |
Manufacturer: | FKuR Kunststoff GmbH |
Trademark: | Terralene® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 8BQRK1_Terralene-LL-1303.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Linear low density polyethylene, butene copolymer, blended with low-density polyethylene. Suitable for extrusion coating and lamination applications. |
General Information | |
---|---|
Features |
|
Uses |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 0.919 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.4 to 3.0 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 3.20 to 4.00 | cm³/10min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 200 | MPa | ISO 527-2 |
Tensile Stress | ISO 527-2 | ||
Yield | 15.0 | MPa | |
Break | 14.0 | MPa | |
Tensile Strain | ISO 527-2 | ||
Yield | 480 | % | |
Break | > 480 | % | |
Flexural Modulus | 180 | MPa | ISO 178 |
Flexural Stress (3.5% Strain) | 5.70 | MPa | ISO 178 |
Flexural Strain at Break | No break | % | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | 68 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
Melting Temperature | 130 to 145 | °C | ISO 3146 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SABIC® LLDPE 518N | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
Starex BF-0677HF | SAMSUNG SDI CO., LTD. | MABS | Starex |
Akulon® XP36-D1H | DSM Engineering Plastics | Nylon 6 | Akulon® |
TECHNYL® A 50X1 NATURAL | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
LNP™ VERTON™ RV00CESS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |