Kingfa PP-V15
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8BMHgi_Kingfa-PP-V15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PP-V15 is a polypropylene material, which contains 20% calcium carbonate filler. This product is available in North America or Asia Pacific,. The main features of Kingfa PP-V15 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.2 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 92 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1410 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 37.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 118 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 20% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP316M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Moplen BA238A | PolyMirae | PP Copolymer | Moplen |
| Anjacom® 050/45 | Almaak International GmbH | PC+ABS | Anjacom® |
| DOMAMID® 66B40 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Durethan® AKV 30 H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |