SEPAZ™ VL140
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8BFQyl_SEPAZ-VL140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™VL140 is a polyxylene amide (PPA) product,. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus 3 | 7160 | MPa | ASTM D790 |
| Flexural Strength 4 | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 306 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | °C | ASTM D648 |
| Peak Melting Temperature | 320 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 305 - 325 | °C | |
| Front Temperature | 310 - 330 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 310 - 330 | °C | |
| Mold Temperature | 70.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Speed: 40 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 FR | RTP Company | PP, Unspecified | RTP |
| Surlyn® PC2000 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| Yuyao PPO N100A | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Adell PP RR-18 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Plaslube® PPS-1305/TF/20/NAT | Techmer Engineered Solutions | PPS | Plaslube® |