Boltaron 9815M
| Category: | PMMA+PVC , Acrylic (PMMA) + PVC |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8AxG5i_Boltaron-9815M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greater impact resistance than competitive 65/65-rated PVC/Acrylic metallic sheets, plus integral color for unsurpassed scratch resistance Boltaron 9815M is a proprietary, fire retardant, extruded PVC/Acrylic alloy for aircraft interior components that meets stringent FAA requirements for flammability, smoke generation and heat release while exhibiting exceptional physical properties. It offers Izod Impact resistance of 5.0 ft lbs/in. (265 J/m)- higher than competitive 65/65- compliant sheets rated at 3.0 ft lbs/in. (159 J/m)- as well as extreme formability, consistent surface quality, and an unlimited range of colors. And unlike FAR 25.853 (d) rated sheet that is reverse-printed with metallic ink on clear cap film laminated to dissimilar substrate material, Boltaron 9815M is comprised of a cap film with integral metallic coloration, permanently fused to a matching "9815-grade" substrate of a complementary solid color, preventing de-lamination and offering unsurpassed scratch resistance. Since the 9815M monolithic cap film is a "metallized" version of Boltaron's 9815 solid color substrate, metallic color selection is unlimited. Boltaron 9815M is specified by the world's leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, fabricated and machined interior components of unequalled durability and metallic appearance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 37.9 | MPa | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 76.7 | °C | ASTM D648 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | Pass | FAR 25.853 | |
| Heat Release | FAR 25.853 | ||
| 2 min | < 65 | kW·min/m² | |
| Peak | < 65 | kW/m² |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ds | ASTM F814 | ||
| 1.5 min | < 100 | ||
| 4 min | < 200 | ||
| Forming Temperature | 168 to 188 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7500 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| TORZEN® T3000HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Nycal™ 1850T3 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| apilon 52® 4511 | API SpA | TPU-Polyester | apilon 52® |
| Karina CLEAR PVC COMP. CRISTAL -E 85/205-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |