LNP™ THERMOCOMP™ ZFM62P compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ASMyg_LNP-THERMOCOMP-ZFM62P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZFM62P is a compound based on PPO resin containing 10% Glass Fiber, 30% Mical. Added feature of this material is: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound ZFM-3362 EP Product reorder name: ZFM62P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.45 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8980 | MPa | ASTM D638 |
| -- | 8550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 76.0 | MPa | ASTM D638 |
| Break | 66.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.4 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8740 | MPa | ASTM D790 |
| -- | 8690 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 124 | MPa | ASTM D790 |
| -- | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D4812 |
| 23°C 3 | 13 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.13 | J | ASTM D3763 |
| -- | 1.41 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 139 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® MV 10 | Versalis S.p.A. | LDPE | Riblene® |
| TEKNIFLEX® VPA7400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Flontech® FT-CAR23-GR2-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hyundai EP Adhesives LE100A/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| Sylvin 8950-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |